WANG Qi-kun, HU Hai-feng, JIAN Ke, CHEN Zhao-hui, ZHENG Wen-wei, MA Qing-song. 先驱体转化法制备2D Cf/SiC-Cu复合材料及其性能. New Carbon Mater., 2006, 21(02): 151-155.
Citation: WANG Qi-kun, HU Hai-feng, JIAN Ke, CHEN Zhao-hui, ZHENG Wen-wei, MA Qing-song. 先驱体转化法制备2D Cf/SiC-Cu复合材料及其性能. New Carbon Mater., 2006, 21(02): 151-155.

先驱体转化法制备2D Cf/SiC-Cu复合材料及其性能

More Information
  • Corresponding author: WANG Qi-kun
  • Received Date: 2005-12-01
  • Accepted Date: 2006-06-20
  • Rev Recd Date: 2006-05-05
  • Publish Date: 2006-06-20
  • In order to meet the working requirements of a solid rocket nozzle throat, the anti-ablative properties of 2D Cf/SiC composites have been improved by decreasing surface temperature by Cu boil off in ablative conditions. 2D Cf/SiC-Cu composites with different Cu contents (2.18vol%,4.86vol%,6.53vol %) were prepared via precursor infiltration and pyrolysis, and their mechanical and ablative properties were investigated. Results indicated that with increasing Cu content, the flexural strength decreased from 261.07MPa to 203.61MPa to 164.91MPa, and the fracture toughness also decreased from 13.4MPa·m1/2 to 12.5MPa·m1/2 to 11.8 MPa·m1/2. The composites all retained structural integrity after 30 seconds ablation in an oxyacetylene torch, but flexural strength decreased to 121.16Mpa to 140.23MPa to 122.87MPa, and the corresponding mass ablations were 0.036g/s, 0.050g/s and 0.064g/s. The 2D Cf/SiC-Cu composites have low density, high strength and low ablative loss compared with other throat materials.
  • loading
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Article Metrics

    Article Views(2338) PDF Downloads(1406) Cited by()
    Proportional views
    Related

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return