WU Jungfeng, BAI Shuo, CHENG Huiming. 热处理对各向同性热解炭材料微观结构和力学性能的影响. New Carbon Mater., 2006, 21(03): 225-230.
Citation: WU Jungfeng, BAI Shuo, CHENG Huiming. 热处理对各向同性热解炭材料微观结构和力学性能的影响. New Carbon Mater., 2006, 21(03): 225-230.

热处理对各向同性热解炭材料微观结构和力学性能的影响

More Information
  • Corresponding author: BAI Shuo
  • Received Date: 2006-05-17
  • Accepted Date: 2006-09-20
  • Rev Recd Date: 2006-08-26
  • Publish Date: 2006-09-20
  • The influence of heat treatment on the microstructure and mechanical properties of isotropic pyrolytic carbon prepared by chemical vapor deposition was studied by TEM, SEM, XRD, polarized light metallography, laser Raman spectroscopy, microhardness and threepoint bend tests. Results show that the interlayer spacing of the pyrolytic carbon decreases and the crystal size increases with increasing heat treatment temperature. At the same time, the microhardness and the elastic modulus decrease with increasing heat treatment temperature. Heat treatment below 2400℃ has no effect on the flexural strength of the isotropic pyrolytic carbon,but its flexural strength increases after graphitization at 2600℃. It is observed that the high temperature heat treatment has changed the pore structure, which consequently influences the mechanical properties.
  • loading
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Article Metrics

    Article Views(2954) PDF Downloads(3369) Cited by()
    Proportional views
    Related

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return