摘要: 将PAN预氧化纤维在400℃~900℃炭化, 经CO2活化得到一系列活性炭纤维，表征了其比表面、孔容和孔径分布等微结构参数, 研究了炭化温度对CO2活化PAN基活性炭纤维微结构的影响。结果表明，炭化温度对活性炭纤维的比表面和孔结构有显著影响, 适中的炭化温度（600℃）有利于得到高比表面积、大的孔容和孔径。Abstract: A series of activated carbon fibers (ACFs) was prepared by carbonizing pre-oxidized PAN fibers at temperatures ranging from 400 to 900℃ followed by CO2 activation and the effect of carbonization temperature on the porous structure of polyarcylonitrile (PAN)-based ACFs characterized by nitrogen adsorption was investigated. It is found that the porous structure of PAN-ACF depends strongly on the carbonization temperature, and a moderate carbonization temperature (600℃) is favorable to obtain ACFs with higher specific surface area, larger pore volume and larger pore size.
-
Key words:
- Activated carbon fibers /
- Carbonization /
- Temperature /
- Microstructure
-