烟煤衍生炭材料的炭化机制及其在锂/钠离子电池中的应用

TIAN Qing-qing; LI Xiao-ming; XIE Li-jing; SU Fang-yuan; YI Zong-lin; DONG Liang; CHEN Cheng-meng

doi:10.1016/S1872-5805(23)60759-0

烟煤衍生炭材料的炭化机制及其在锂/钠离子电池中的应用

doi: 10.1016/S1872-5805(23)60759-0

田青青^{1, 3,},
李晓明²,
谢莉婧²,
苏方远²,
易宗琳²,
董良^{1, 3, ,},
陈成猛^2, ,

1.
中国矿业大学煤炭加工与高效洁净利用教育部重点实验室，江苏徐州 221116
2.
中国科学院山西煤炭化学研究所炭材料重点实验室，山西太原 030001
3.
中国矿业大学化工学院，江苏徐州 221116

基金项目: 陕西省自然科学基础研究计划 (2019JLZ-10)；国家自然科学基金委员会面上基金项目 (22179139)；山西省基础研究计划面上基金项目 (20210302123008, 20210302124101)；山西省重点研发计划项目 (2022ZDYF028)

详细信息

通讯作者:
董　良，教授. E-mail：dongl@cumt.edu.cn

陈成猛，研究员. E-mail：ccm@sxicc.ac.cn

中图分类号: 127.1⁺1
计量
- 文章访问数: 452
- HTML全文浏览量: 164
- PDF下载量: 153
- 被引次数: 0
出版历程
- 收稿日期: 2023-03-07
- 录用日期: 2023-06-12
- 修回日期: 2023-06-12
- 网络出版日期: 2023-06-16
- 刊出日期: 2023-10-01

Insights into the carbonization mechanism of bituminous coal-derived carbon materials for lithium-ion and sodium-ion batteries

1.
Key Laboratory of Coal Processing and Efficient Utilization, China University of Mining and Technology, Xuzhou 221116, China
2.
CAS Key Laboratory of Carbon Materials, Institute of Coal Chemistry, Chinese Academy of Sciences, Taiyuan 030001, China
3.
School of Chemical Engineering & Technology, China University of Mining & Technology, Xuzhou 221116, China

More Information

Author Bio:
田青青，硕士研究生. E-mail：tianqingqing032@163.com

Corresponding author: DONG Liang. E-mail: dongl@cumt.edu.cn; CHEN Cheng-meng. E-mail: ccm@sxicc.ac.cn

摘要

摘要: 近年来，人们对利用低温炭化工艺制备煤基无定形炭材料作为锂离子电池（LIBs）和钠离子电池（SIBs）的负极材料产生了兴趣。然而，煤衍生炭材料的炭化机制仍然不太清楚。因此，本文选取烟煤为原料，探究了煤炭到无定形炭材料的化学、微晶和孔隙结构演变过程。随着温度的升高（低于1 000 ℃），材料结构发生局部变化，碳层的迁移和小分子物质的释放导致了层间距（3.69-3.82 Å）和缺陷密度（1.26-1.90）逐渐增大，并且产生了丰富的纳米微孔结构。当温度升至1000~1600 °C时，层间距和缺陷密度开始逐渐减小。在LIBs中，经1 000 °C炭化制备的样品表现出最佳的电化学性能。在0.1 C倍率测试下可逆容量达到384 mAh g^–1，在5 C倍率下仍能保持170 mAh g^–1，表现出优异的倍率性能。在SIBs中，经1200 °C炭化制备的样品在0.1 C倍率测试下具有270.1 mAh g^–1的可逆容量和高达86.8%的首次库伦效率。本研究为煤基炭材料的精细化制备提供了理论支撑。
- 煤 /
- 炭化机制 /
- 炭材料 /
- 锂离子电池 /
- 钠离子电池
Abstract: Despite recent interest in the low-temperature carbonization of coal to prepare disordered carbon materials for the anodes of lithium-ion (LIBs) and sodium-ion batteries (SIBs), the carbonization mechanism is still poorly understood. We selected bituminous coal as the raw material and investigated the chemical, microcrystal, and pore structure changes during the carbonization process from coal to the resulting disordered carbon. These structural changes with temperature below 1 000 °C show an increase in both interlayer spacing (3.69–3.82 Å) and defect concentration (1.26–1.90), accompanied by the generation of a large amount of nano-microporous materials. These changes are attributed to the migration of the local carbon layer and the release of small molecules. Furthermore, a decrease in interlayer spacing and defect concentration occurs between 1 000 °C and 1 600 °C. In LIBs, samples carbonized at 1000 °C showed the best electrochemical performance, with a reversible capacity of 384 mAh g⁻¹ at 0.1 C and excellent rate performance, maintaining 170 mAh g⁻¹ at 5 C. In SIBs, samples carbonized at 1 200 °C had a reversible capacity of 270.1 mAh g⁻¹ at 0.1 C and a high initial Coulombic efficiency of 86.8%. This study offers theoretical support for refining the preparation of carbon materials derived from coal.
- Coal /
- Carbonization mechanism /
- Carbon materials /
- Lithium-ion batteries /
- Sodium-ion batteries

HTML全文

FIG. 2656. FIG. 2656.

FIG. 2656.. FIG. 2656.

下载: 全尺寸图片幻灯片

Figure 1. (a) TG-DTG curves of CC. (b) MS spectra of evolving gas from TG of CC. (c) O/C and H/C atomic ratio of CC and coal-derived disordered carbon materials. (d) FTIR spectrum, and (e) High-resolution O1s spectra of CC and coal-derived disordered carbon materials at different carbonization temperatures

下载: 全尺寸图片幻灯片

Figure 2. (a-f) HR-TEM and SAED images of coal-derived disordered carbon materials. (g) Schematic illustration of the structural transformation from a highly-disordered state to a graphite-like structure

下载: 全尺寸图片幻灯片

Figure 3. (a) XRD patterns of CC and coal-derived disordered carbon materials. (b) Schematic definition of the parameter R. (c) Variation curve of R values of CC and coal-derived disordered carbon materials at different carbonization temperatures. (d) Fitted Raman spectra, (e) Values of d₀₀₂ and A_D1/A_G, (f) N₂ adsorption-desorption isotherms, and (g) total open pore volume and average pore diameter of CC and coal-derived disordered carbon materials

下载: 全尺寸图片幻灯片

Figure 4. (a) GCD curves at 0.1C, (b) Variation curve of specific capacity and ICE, and (c) Rate capacity at different current rates of coal-derived disordered carbon materials. (d) The three CV curves of CC-600, CC-1000 and CC-1400. (e) The CV curves at different rates of CC-1000. (f) A linear relationship between log (Peak Currents) and log (Sweep Rate), (g) Nyquist plots of the fresh cells of coal-derived disordered carbon materials. (h) GITT curves of the CC-1000 during the discharge/charge process in LIBs

下载: 全尺寸图片幻灯片

Figure 5. (a) GCD curves at 0.1C, (b) Variation curve of specific capacity and ICE, and (c) Rate capacity at different current rates of coal-derived disordered carbon materials. (d) The 3 CV curves of CC-600, CC-1200 and CC-1400. (e) The CV curves at different rates of CC-1200. (f) A linear relationship between log (Peak Currents) and log (Sweep Rate), (g) Nyquist plots of the fresh cells of coal-derived disordered carbon materials. (h) GITT curves of the CC-1200 in SIBs

下载: 全尺寸图片幻灯片

Figure 6. Possible carbonization mechanism of coal and the correlated structure-performance relationship in LIBs and SIBs

下载: 全尺寸图片幻灯片

Table 1. The contents of O1s peaks of coal-derived disordered carbon materials

B.E. (eV)	Assignment	CC	CC-600	CC-800	CC-1000	CC-1200	CC-1400	CC-1600
534.8	O―H	1.03	1.05	1.08	1.00	1.24	1.30	0.93
533.4	C―O	5.50	3.48	2.27	2.69	2.52	2.09	2.07
532.1	C＝O	6.85	2.35	1.95	2.42	2.01	1.77	1.84

下载: 导出CSV

Table 2. Physical parameters of coal-derived disordered carbon materials

Sample	CC	CC-600	CC-800	CC-1000	CC-1200	CC-1400	CC-1600
R	2.03	1.50	1.90	2.17	2.20	2.35	3.17
2θ (°)	24.12	24.00	23.54	23.29	23.54	23.72	24.78
d₀₀₂ (Å)	3.69	3.71	3.78	3.82	3.78	3.75	3.59
A_D1/A_G	1.26	1.72	1.73	1.90	1.73	1.50	1.49

下载: 导出CSV

Table 3. Pore structure parameters of coal-derived disordered carbon materials

Sample	S_BET^a (m² g^–1)	V_tot^a (cm³ g^–1)	D_ave^a (nm)	Ture density^b (g cm^–3)	V_{close pores} (cm³ g^–1)	S_BET^c (m² g^–1)
CC	2.72	0.0080	11.71	1.36	0.29	133.70
CC-600	272.97	0.0152	2.23	1.55	0.20	289.28
CC-800	38.56	0.0249	2.59	1.79	0.11	318.95
CC-1000	4.14	0.0073	7.06	1.85	0.10	293.47
CC-1200	2.03	0.0067	13.13	1.98	0.06	81.49
CC-1400	2.11	0.0069	13.07	1.73	0.14	2.55
CC-1600	2.36	0.0080	13.47	1.54	0.21	1.69
Note: ^a Testing under N₂ atmosphere. ^b Testing under He atmosphere. ^c Testing under CO₂ atmosphere.

下载: 导出CSV

参考文献(54)

[1]	Xing B L, Zeng H H, Huang G X, et al. Porous graphene prepared from anthracite as high performance anode materials for lithium-ion battery applications[J]. Journal of Alloys and Compounds,2019,779:202-211. doi: 10.1016/j.jallcom.2018.11.288
[2]	Gao S J, Liu W F, Fu D J, et al. Research progress on recovering the components of spent Li-ion batteries[J]. New Carbon Materials,2022,37(3):435-460. doi: 10.1016/S1872–5805(22)60605–X
[3]	Slater M D, Kim D H, Lee E, et al. Sodium-ion batteries[J]. Advanced Functional Materials,2013,23:947-958. doi: 10.1002/adfm.201200691
[4]	Scrosati B, Garche J. Lithium batteries: Status, prospects and future[J]. Journal of Power Sources,2010,195:2419-2430. doi: 10.1016/j.jpowsour.2009.11.048
[5]	Xie L J, Tang C, Bi Z H, et al. Hard carbon anodes for next-generation Li-ion batteries: Review and perspective[J]. Advanced Energy Materials,2021,11(38):2101650. doi: 10.1002/aenm.202101650
[6]	Udod I A. Sodium-graphite intercalation compound of the first stage: Two-dimensional structure and stability[J]. Synthetic Metals,1997,88(2):127-131. doi: 10.1016/S0379–6779(97)80890–9
[7]	Stevens D A, Dahn J R. The mechanisms of lithium and sodium insertion in carbon materials[J]. Journal of the Electrochemical Society,2001,148(48):803-811. doi: 10.1149/1.1379565
[8]	Yuan Y, Chen Z W, Yu H X, et al. Heteroatom-doped carbon-based materials for lithium and sodium ion batteries[J]. Energy Storage Materials,2020,32:65-90. doi: 10.1016/j.ensm.2020.07.027
[9]	Ding J, Wang H L, Li Z, et al. Carbon nanosheet frameworks derived from peat moss as high performance sodium ion battery anodes[J]. ACS Nano,2013,7(12):11004-11015. doi: 10.1021/nn404640c
[10]	Cheng J Y, Yi Z L, Wang Z B, et al. Towards optimized Li-ion storage performance: Insight on the oxygen species evolution of hard carbon by H₂ reduction[J]. Electrochimica Acta,2020,337(20):135736. doi: 10.1016/j.electacta.2020.135736
[11]	Yu J L, Tahmasebi A, Han Y N, et al. A review on water in low rank coals: The existence, interaction with coal structure and effects on coal utilization[J]. Fuel Processing Technology,2013,106:9-20. doi: 10.1016/j.fuproc.2012.09.051
[12]	Peng Z F, Ning X J, Wang G W, et al. Structural characteristics and flammability of low-order coal pyrolysis semi-coke[J]. Journal of the Energy Institute,2020,93(4):1341-1353. doi: 10.1016/j.joei.2019.12.004
[13]	Shi M, Song C L, Tai Z G, et al. Coal-derived synthetic graphite with high specific capacity and excellent cyclic stability as anode material for lithium-ion batteries[J]. Fuel,2021,292:120250. doi: 10.1016/j.fuel.2021.120250
[14]	Xing B L, Zhang C T, Cao Y J, et al. Preparation of synthetic graphite from bituminous coal as anode materials for high performance lithium-ion batteries[J]. Fuel Processing Technology,2018,172:162-171. doi: 10.1016/j.fuproc.2017.12.018
[15]	Ehrburger P, Addoun A, Addoun F, et al. Carbonization of coals in the presence of alkaline hydroxides and carbonates: Formation of activated carbons[J]. Fuel,1986,65(10):1447-1449. doi: 10.1016/0016–2361(86)90121–3
[16]	Hsu L Y, Teng H S. Influence of different chemical reagents on the preparation of activated carbons from bituminous coal[J]. Fuel Processing Technology,2000,64(1):155-166. doi: 10.1016/S0378–3820(00)00071–0
[17]	Zhao H Y, Wang L X, Jia D Z, et al. Coal based activated carbon nanofibers prepared by electrospinning[J]. Journal of Materials Chemistry A,2014,2(24):9338-9344. doi: 10.1039/C4TA00069B
[18]	Gao F, Qu J Y, Zhao Z B, et al. A green strategy for the synthesis of graphene supported Mn₃O₄ nanocomposites from graphitized coal and their supercapacitor application[J]. Carbon,2014,80:640-650. doi: 10.1016/j.carbon.2014.09.008
[19]	Zhang T K, Wang Q, Li G Q, et al. Formation of carbon nanotubes from potassium catalyzed pyrolysis of bituminous coal[J]. Fuel,2019,239:230-238. doi: 10.1016/j.fuel.2018.11.010
[20]	Moothi K, Lyuke S E, Meyyappan M, et al. Coal as a carbon source for carbon nanotube synthesis[J]. Carbon,2012,50(8):2679-2690. doi: 10.1016/j.carbon.2012.02.048
[21]	Sun W J, Wang N, Chu W, et al. The role of volatiles and coal structural variation in coal methane adsorption[J]. Science Bulletin,2015,60(5):532-540. doi: 10.1007/s11434–015–0747–6
[22]	Porada S. The reactions of formation of selected gas products during coal pyrolysis[J]. Fuel,2004,83(9):1191-1196. doi: 10.1016/j.fuel.2003.11.007
[23]	Li J, Cao Y L, Wang L X, et al. Cost-effective synthesis of bamboo-structure carbon nanotubes from coal for reversible lithium storage[J]. RSC Advances,2017,7:34770-34775. doi: 10.1039/C7RA04047D
[24]	He X J, Zhang H B, Zhang H, et al. Direct synthesis of 3D hollow porous graphene balls from coal tar pitch for high performance supercapacitors[J]. Journal of Materials Chemistry A,2014,2(46):19633-19640. doi: 10.1039/C4TA03323J
[25]	Zhao X J, Jia W, Wu X Y, et al. Ultrafine MoO₃ anchored in coal-based carbon nanofibers as anode for advanced lithium-ion batteries[J]. Carbon,2020,156:445-452. doi: 10.1016/j.carbon.2019.09.065
[26]	Li M Y, Tsai W Y, Thapaliya B P, et al. Modified coal char materials with high rate performance for battery applications[J]. Carbon,2021,172:414-421. doi: 10.1016/j.carbon.2020.10.035
[27]	Wang K F, Sun F, Wang H, et al. Altering thermal transformation pathway to create closed pores in coal-derived hard carbon and boosting of Na⁺ plateau storage for high-performance sodium-ion battery and sodium-ion capacitor[J]. Advanced Functional Materials,2022,32(34):2203725. doi: 10.1002/adfm.202203725
[28]	Wang Y H, Yang W, Yan F Z, et al. Study on coal molecular structure characteristics on methane adsorption performance under pyrolysis treatment[J]. Fuel,2022,328:125228. doi: 10.1016/j.fuel.2022.125228
[29]	Yang W, Wang Y H, Yan F Z, et al. Evolution characteristics of coal microstructure and its influence on methane adsorption capacity under high temperature pyrolysis[J]. Energy,2020,254:124262. doi: 10.1016/j.energy.2022.124262
[30]	Hu J H, Chen Y Q, Qian K Z, et al. Evolution of char structure during mengdong coal pyrolysis: Influence of temperature and K₂CO₃[J]. Fuel Processing Technology,2017,159:178-186. doi: 10.1016/j.fuproc.2017.01.042
[31]	Li Y, Wang Z H, Huang Z Y, et al. Effect of pyrolysis temperature on lignite char properties and slurrying ability[J]. Fuel Processing Technology,2015,134:52-58. doi: 10.1016/j.fuproc.2015.01.007
[32]	Chen Y Y, Mastalerz M, Schimmelmann A. Characterization of chemical functional groups in macerals across different coal ranks via micro-FTIR spectroscopy[J]. International Journal of Coal Geology,2012,104:22-33. doi: 10.1016/j.coal.2012.09.001
[33]	Zhang K, Li Y, Wang Z H, et al. Pyrolysis behavior of a typical Chinese sub-bituminous Zhundong coal from moderate to high temperatures[J]. Fuel,2016,185:701-708. doi: 10.1016/j.fuel.2016.08.038
[34]	Qi Y R, Lu Y X, Ding F X, et al. Slope-dominated carbon anode with high specific capacity and superior rate capability for high safety Na-ion batteries[J]. Angewandte Chemie, International Edition,2019,58(13):4361-4365. doi: 10.1002/anie.201900005
[35]	Song M X, Yi Z L, Xu R, et al. Towards enhanced sodium storage of hard carbon anodes: Regulating the oxygen content in precursor by low-temperature hydrogen reduction[J]. Energy Storage Materials,2022,51:620-629. doi: 10.1016/j.ensm.2022.07.005
[36]	Li Z Q, Lu C J, Xia Z P, et al. X-ray diffraction patterns of graphite and turbostratic carbon[J]. Carbon,2007,45(8):1686-1695. doi: 10.1016/j.carbon.2007.03.038
[37]	Zheng T, Xing W, Dahn J R. Carbons prepared from coals for anodes of lithium-ion cells[J]. Carbon,1996,34(12):1501-1507. doi: 10.1016/S0008–6223(96)00098–X
[38]	Dahn J R, Xing W, Gao Y. The “falling cards model” for the structure of microporous carbons[J]. Carbon,1997,35(6):825-830. doi: 10.1016/S0008–6223(97)00037–7
[39]	Sadezky A, Muckenhuber H, Grothe H, et al. Raman microspectroscopy of soot and related carbonaceous materials: Spectral analysis and structural information[J]. Carbon,2005,43(8):1731-1742. doi: 10.1016/j.carbon.2005.02.018
[40]	Meng D X, Yue C Y, Wang T, et al. Evolution of carbon structure and functional group during Shenmu lump coal pyrolysis[J]. Fuel,2021,287:119538. doi: 10.1016/j.fuel.2020.119538
[41]	Xu R S, Zhang J L, Wang G W, et al. Isothermal kinetic analysis on fast pyrolysis of lump coal used in COREX process[J]. Journal of Thermal Analysis and Calorimetry,2016,123:773-783. doi: 10.1007/s10973–015–4972–7
[42]	Liang D C, Xie Q, Wan C R, et al. Evolution of structural and surface chemistry during pyrolysis of Zhundong coal in an entrained-flow bed reactor[J]. Journal of Analytical and Applied Pyrolysis,2019,140:331-338. doi: 10.1016/j.jaap.2019.04.010
[43]	Chen Y X, Xi B J, Huang M, et al. Defect-selectivity and “order-in-disorder” engineering in carbon for durable and fast potassium storage[J]. Advanced Materials,2022,34(7):2108621. doi: 10.1002/adma.202108621
[44]	Li X J, Hayashi J I, Li C Z. FT-Raman spectroscopic study of the evolution of char structure during the pyrolysis of a Victorian brown coal[J]. Fuel,2006,85(12-13):1700-1707. doi: 10.1016/j.fuel.2006.03.008
[45]	Chen M, Yu H W, Chen J H, et al. Effect of purification treatment on adsorption characteristics of carbon nanotubes[J]. Diamond and Related Materials,2007,16(4-7):1110-1115. doi: 10.1016/j.diamond.2006.12.061
[46]	Buiel E R, George A E, Dahn J R. Model of micropore closure in hard carbon prepared from sucrose[J]. Carbon,1999,37:1399-1407. doi: 10.1016/S0008–6223(98)00335–2
[47]	Ji H J, Mao Y N, Su H T. Effects of organic micromolecules in bituminous coal on its microscopic pore characteristics[J]. Fuel,2020,262:116529. doi: 10.1016/j.fuel.2019.116529
[48]	Evanoff K, Magasinski A, Yang J B, et al. Nanosilicon-coated graphene granules as anodes for Li-ion batteries[J]. Advanced Energy Materials,2011,1(4):495-498. doi: 10.1002/aenm.201100071
[49]	Sun Z F, Chen Y X, Xi B J, et al. Edge-oxidation-induced densification towards hybrid bulk carbon for low-voltage, reversible and fast potassium storage[J]. Energy Storage Materials,2022,53:482-491. doi: 10.1016/j.ensm.2022.09.031
[50]	Liu Y, Dai H D, Wu L, et al. A large scalable and low-cost sulfur/nitrogen dual-doped hard carbon as the negative electrode material for high-performance potassium-ion batteries[J]. Advanced Energy Materials,2019,9(34):1901379. doi: 10.1002/aenm.201901379
[51]	Ruan J F, Zhao Y H, Luo S N, et al. Fast and stable potassium-ion storage achieved by in situ molecular self-assembling N/O dual-doped carbon network[J]. Energy Storage Materials,2019,23:46-54. doi: 10.1016/j.ensm.2019.05.037
[52]	Cao B, Liu H, Xu B, et al. Mesoporous soft carbon as an anode material for sodium ion batteries with superior rate and cycling performance[J]. Journal of Materials Chemistry A,2016,4(17):6472-6478. doi: 10.1039/C6TA00950F
[53]	Sun N, Guan Z R X, Liu Y W, et al. Extended “adsorption-insertion” model: a new insight into the sodium storage mechanism of hard carbons[J]. Advanced Energy Materials,2019,9(32):1901351. doi: 10.1002/aenm.201901351
[54]	Jin Y, Sun S X, Ou M Y, et al. High-performance hard carbon anode: tunable local structures and sodium storage mechanism[J]. ACS Applied Energy Materials,2018,1(5):2295-2305. doi: 10.1021/acsaem.8b00354