以含模板剂的中孔MCM-41为模板合成类碳纳米管材料

LIU Xian-bin; LIU Zhong-min; CHANG Fu-xiang; QU Li-hong; SANG Shi-yun; ZHANG Yang-yang

Article Contents

Article Navigation > New Carbon Mater. > 2006 > 21(03): 237-242

LIU Xian-bin, LIU Zhong-min, CHANG Fu-xiang, QU Li-hong, SANG Shi-yun, ZHANG Yang-yang. 以含模板剂的中孔MCM-41为模板合成类碳纳米管材料. New Carbon Mater., 2006, 21(03): 237-242.

Citation:

LIU Xian-bin, LIU Zhong-min, CHANG Fu-xiang, QU Li-hong, SANG Shi-yun, ZHANG Yang-yang. 以含模板剂的中孔MCM-41为模板合成类碳纳米管材料. New Carbon Mater., 2006, 21(03): 237-242.

LIU Xian-bin, LIU Zhong-min, CHANG Fu-xiang, QU Li-hong, SANG Shi-yun, ZHANG Yang-yang. 以含模板剂的中孔MCM-41为模板合成类碳纳米管材料. New Carbon Mater., 2006, 21(03): 237-242.

Citation:

LIU Xian-bin, LIU Zhong-min, CHANG Fu-xiang, QU Li-hong, SANG Shi-yun, ZHANG Yang-yang. 以含模板剂的中孔MCM-41为模板合成类碳纳米管材料. New Carbon Mater., 2006, 21(03): 237-242.

PDF( 198 KB)

以含模板剂的中孔MCM-41为模板合成类碳纳米管材料

Dalian Institute of Chemical Physics, Chinese Academy of Sciences, Dalian 116023, LiaoNing, China

More Information

Corresponding author: LIU Zhong-min
Received Date: 2005-10-14
Accepted Date: 2006-09-20
Rev Recd Date: 2006-05-15
Publish Date: 2006-09-20

Abstract

Abstract

A carbon nanotube analog was prepared using the structuredirecting agent cetyltrimetylammonium bromide locked in the channels of MCM41 as a carbon source. The structures and properties of the resulting samples were characterized by powder XRD, nitrogen adsorptiondesorption measurement, TEM and TGA. It was found that the carbon nanotube analog obtained by this method is amorphous. Pretreatment with concentrated sulfuric acid is a key step in its formation.
- MCM-41,
- Template,
- Analogous carbon nanotube