Key Laboratory of Interface Science and Engineering Advance Materials of Taiyuan University of Technology,Ministry of Education,Taiyuan 030024,China; 2.College of Materials Science and Engineering,Taiyuan University of Technology,Taiyuan 030024,China; 3.College of Chemistry and Chemical Engineering,Taiyuan University of Technology, Taiyuan 030024,China
Deoiled asphalt was chosen as the carbon source and FeCl3 as the catalyst, to prepare vapor-grown carbon fibers (VGCFs) with different morphologies, by chemical vapor deposition, in an atmosphere of argon and hydrogen. The influence of reaction time (10, 20, 25, 30, and 40min) on the morphologies and structures of products at 1100℃ was discussed. The morphologies and structures of the products were characterized by field-emission scanning electron microscopy, high resolution transmission electron microscopy, X-ray diffraction and Raman spectroscopy. Results showed that the VGCFs became relatively straight and then interpenetrating. The diameters of the VGCFs were 1.0 to 1.2μm, 250 to 300nm, 350 to 400nm, and 700 to 800nm when the reaction time was 10, 20, 25, 30, and 40min, respectively. In addition, V-shaped VGCFs were observed.
DownLoad: