GUAN Yi-biao, WU Feng, BAI Ying, WU Chuan. Modification of a LiFePO4 cathode for lithium ion batteries by carbon coating and copper doping. New Carbon Mater., 2009, 24(04): 359-363.
Citation:
GUAN Yi-biao, WU Feng, BAI Ying, WU Chuan. Modification of a LiFePO4 cathode for lithium ion batteries by carbon coating and copper doping. New Carbon Mater., 2009, 24(04): 359-363.
GUAN Yi-biao, WU Feng, BAI Ying, WU Chuan. Modification of a LiFePO4 cathode for lithium ion batteries by carbon coating and copper doping. New Carbon Mater., 2009, 24(04): 359-363.
Citation:
GUAN Yi-biao, WU Feng, BAI Ying, WU Chuan. Modification of a LiFePO4 cathode for lithium ion batteries by carbon coating and copper doping. New Carbon Mater., 2009, 24(04): 359-363.
The effects of a carbon coating and copper doping on the electrochemical performance and tap density of a LiFePO4 cathode for lithium ion batteries were investigated by XRD, SEM, charge/discharge cycle tests, rate tests and tap density tests. Results showed that the average discharge capacity of LiFePO4/C and LiFe0.95Cu0.05PO4 were 147mAh/g and 131mAh/g respectively. The capacity fading rate of LiFe0.95Cu0.05PO4 was much larger than that of LiFePO4/C in a high-rate discharging test. The electrochemical performance of LiFePO4/C was better than that of LiFe0.95Cu0.05PO4, but the tap density of the latter was 1.5 times as large as that of the former.