AN Feng, LU Chun-xiang, GUO Jin-hai, HE Shu-qing, LU Hui-bin, YANG. Preparation of a carbon nanotube/carbon fiber hybrid and its wettability with epoxy. New Carbon Mater., 2011, 26(5): 361-367.
Citation:
AN Feng, LU Chun-xiang, GUO Jin-hai, HE Shu-qing, LU Hui-bin, YANG. Preparation of a carbon nanotube/carbon fiber hybrid and its wettability with epoxy . New Carbon Mater., 2011, 26(5): 361-367.
AN Feng, LU Chun-xiang, GUO Jin-hai, HE Shu-qing, LU Hui-bin, YANG. Preparation of a carbon nanotube/carbon fiber hybrid and its wettability with epoxy. New Carbon Mater., 2011, 26(5): 361-367.
Citation:
AN Feng, LU Chun-xiang, GUO Jin-hai, HE Shu-qing, LU Hui-bin, YANG. Preparation of a carbon nanotube/carbon fiber hybrid and its wettability with epoxy . New Carbon Mater., 2011, 26(5): 361-367.
A carbon nanotube/carbon fiber (CNT/CF) hybrid was prepared via an aerosol-assisted chemical vapor deposition (AACVD) method using acetylene as carbon source and ferrocene as catalyst. The morphology and microstructure of the CNT/CF hybrid were characterized by SEM and TEM. It was found that CNTs were uniformly and densely grown onto CFs at 750-800℃ for 30min. Results obtained from single fiber tests showed that the tensile strength of the CNT/CF hybrid decreased by 13% after AACVD at 750-800℃ for 30min compared to that of CFs, however, the tensile degradation was less than 10% after AACVD at 750℃ for 5 to 40min. The wettability of the hybrid with epoxy resin was improved compared with that of the original CFs