A comparative study of the characteristics and carbonization behaviors of three modified coal tar pitches

Funds: Natural Science Foundation of Shaanxi Province (2009GM6001-1).
More Information
  • Received Date: January 13, 2013
  • Revised Date: March 28, 2013
  • Accepted Date: May 07, 2013
  • Coal tar pitch (CTP) was modified either with 10g cinnamaldehyde (CMA) per 100 g CTP, 7 g p-toluene sulfonic acid (PTS) per 100g CTP, or a mixture of 10g CMA and 7 g PTS per 100g CTP. The parent CTP and the modified CTPs were characterized by Fourier transform infrared spectroscopy (FT-IR) and thermogravimetric analysis. The four samples were carbonized at different temperatures and the products were characterized by FT-IR and polarized-light microscopy. Results show that the modifications have a large influence on the characteristics and carbonization behavior of the CTP. The distillation of CMA occurs at a temperature lower than 300 ℃ during the carbonization of the CMA-modified CTP. Methyl and methylene groups of the parent CTP and the modified CTPs gradually disappear with increasing temperature during carbonization. The modification of the CTP with the mixture of CME and PTS results in a highest increase (5.08%) of carbonization yield and the most abundant mesophase sphere formation during carbonization
  • Related Articles

    [1]DONG Ya-wei, XING Guo-zheng, JIN Li-e, LI Ping, CAO Qing. Co-carbonization of brominated petroleum pitch, coal tar pitch and benzoyl chloride to prepare cokes[J]. New Carbon Mater., 2019, 34(3): 258-266. DOI: 10.1016/S1872-5805(19)60015-6
    [2]WANG Mei, JIA Xian-feng, MA Cheng, WANG Ji-tong, SONG Zhen-chao, LONG Dong-hui, QIAO Wen-ming, LING Li-cheng. Adsorption and desorption behavior of benzene and toluene on porous carbon monoliths[J]. New Carbon Mater., 2017, 32(4): 358-364.
    [3]GUO Liang-cheng, JIN Li-e, ZHONG Cun-gui, WANG Ying, CAO Qing. Effects of a dioctyl phthalate addition to coal tar pitch on the microstructures and electrochemical properties of derived semi-cokes[J]. New Carbon Mater., 2017, 32(1): 71-76.
    [4]Michio INAGAKI, Ki Chul PARK, Morinobu ENDO. Carbonization under pressure[J]. New Carbon Mater., 2010, 25(06): 409-420. DOI: 10.1016/S1872-5805(09)60042-1
    [5]WEN Yue-fang, CAO Xia, YANG Yong-gang, LI Hui, GUO Jian-qiang, LIU Lang. PAN预氧化纤维的炭化过程[J]. New Carbon Mater., 2008, 23(02): 121-126.
    [6]XU Bin, WU Feng, CAO Gao-ping, YANG Yu-sheng. 炭化温度对CO2活化PAN基活性炭纤维微结构的影响(英)[J]. New Carbon Mater., 2006, 21(01): 14-18.
    [7]SUN Xin, ZHA Qing-fang, GUO Yan-sheng, LI Zhao-feng. 石油焦系超级活性炭的孔结构控制(英)[J]. New Carbon Mater., 2005, 20(03): 240-244.
    [8]JIANG Ze-hui, ZHANG Dong-sheng, FEI Ben-hua, YUE Yong-de, CHEN Xiao-hong. 炭化温度对竹炭微观结构及电性能的影响[J]. New Carbon Mater., 2004, 19(04): 249-253.
    [9]ZHU Gui-ru, WANG Tong-hua, ZHANG Shou-hai, SONG Cheng-wen, JIAN Xi-gao, CAI Tian-xi. 聚醚砜酮薄膜在炭化过程中化学结构的变化[J]. New Carbon Mater., 2004, 19(01): 49-52.
    [10]HOU Zhao-hui, LI Xin-hai, LIU En-hui, HE Ze-qiang, DENG Ling-feng. 同步合成模板炭化法制备双电层电容器电极用中孔炭材料的研究(英)[J]. New Carbon Mater., 2004, 19(01): 11-15.

Catalog

    Article Metrics

    Article views (1447) PDF downloads (1259) Cited by()
    Related

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return